Tag Archives: Alloy 718

Galvanic corrosion between Inconel fasteners and Monel in seawater

Posted on December 28, 2017 by dean

Q: I am considering using Inconel 718 fasteners with a Monel K-500 flange in seawater. I’m concered as Inconel is the more anodic of the two and is also has a smaller surface area. Would this cause galvanic corrosion? A: This is a great question. In this case if you plan … Continue reading →

Posted in Application, Corrosion Resistance, FAQs, Material, Specialty Metal Fasteners | Tagged , , , , , , , , , , | Leave a comment

Bolt for hot hydrogen sulfide, CO2, hydrocarbons & salt water

Posted on August 9, 2017 by dean

Q: I need a material that will be suitable for oil and gas use. Submersion in hydrogen sulfide, carbon dioxide, hydrocarbons, salt water at temperatures up to 325F. Crevice corrosion has been a factor. Also need 170ksi min tensile strength. Plus we’d like to torque a 3/8-24 fastener to 50 … Continue reading →

Posted in Application, Corrosion Resistance, FAQs, High Strength, Specialty Metal Fasteners, Uncategorized | Tagged , , , , , , , , | Leave a comment

Best bolts for Inconel 625 flanges

Posted on May 18, 2017 by dean

q: What bolting material should be used with Inconel 625 flanges? We used ASTM A193 Gr B7 however noticing some corrosion issues. A: This is a very common problem but to answer it accurately, it depends on the environment that your flanges see and also to a certain extent what … Continue reading →

Posted in Application, Corrosion Resistance, FAQs, Specialty Metal Fasteners | Tagged , , , , , , , , | Leave a comment

Inconel 625 vs. 718 bolts: Which Is Best for Your Application?

Posted on March 6, 2017 by dean

Inconel fasteners are commonly used for extreme environments and come in various “flavors” depending on the needs of the application. This brief paper will give you a quick comparison of the two most popular grades, Inconel 625 and Inconel 718 to help you choose the best material.

Posted in Blog | Tagged , , , , , , , , , , , , | 1 Comment

Precipitation Hardened Bolts: The What & Why?

Posted on November 15, 2016 by dean

So you’ve heard the term, but what is it? Technically, it is a method in which an alloy’s structural matrix is altered on an atomic level by using temperature change to enhance the material’s mechanical properties – increasing the yield and tensile strength. Simply, it is a way to further strengthen a material. It is … Continue reading →

Posted in Blog | Tagged , , , , , , , , , , , , , , , , , , , , | Leave a comment