Posted on August 28, 2017 by dean
Q: Inconel 625 and Hastelloy C276 bolts seem to have similar Nickel content. Does this mean these fasteners will perform the same in a corrosive environment? A: Inconel 625 and Hastelloy C276 bolts do offer similar corrosion resistance but Hastelloy C276 has a slight edge in many acidic environements, especially … Continue reading →
Posted on May 25, 2017 by dean
Q: I’m using zirconium fasteners in a sulfuric acid process but they are showing corrosion. I’m not sure why as I’m well below boiling and only using 40% concentration. There may be some downstream contaminants, but not much. Any ideas? A: It is most likely the contaminants that are causing … Continue reading →
Posted on May 18, 2017 by dean
q: What bolting material should be used with Inconel 625 flanges? We used ASTM A193 Gr B7 however noticing some corrosion issues. A: This is a very common problem but to answer it accurately, it depends on the environment that your flanges see and also to a certain extent what … Continue reading →
Posted on May 11, 2017 by dean
They rhyme, are both used in extreme environments, and are both nickel metal alloys, but Monel and Inconel are actually very different. But how? Let’s start with basic chemistry. Monel is a nickel-copper alloy and Inconel is a nickel-chromium alloy. So what does that mean for your extreme application? We … Continue reading →
Posted on March 6, 2017 by dean
Inconel fasteners are commonly used for extreme environments and come in various “flavors” depending on the needs of the application. This brief paper will give you a quick comparison of the two most popular grades, Inconel 625 and Inconel 718 to help you choose the best material.