Tag Archives: seawater
Posted on November 15, 2017 by dean
Q: I have a high strength application that requires resistance to damp salt air and occasional sea splash, I’m using Monel 400 but it’s not holding up the the 75ksi of yield I need. Lots of broken bolts? Is is corrosion or strength? Thoughts? A: Your issue isn’t the corrosion. … Continue reading →
Posted on November 14, 2017 by dean
Q: Is AL6XN a steel or nickel alloy? Trying to figure out if it would perform as well as Monel in seawater. A: To answer your first question, AL6XN bolts are actually both a nickel and a steel alloy. AL6XN is often described as a high nickel content stainless alloy. Though … Continue reading →
Posted in Application, Corrosion Resistance, FAQs, Material, Specialty Metal Fasteners | Tagged AL-6XN, AL6XN, Alloy 400, Corrosion, Crevice Corrosion, Monel, Monel 400, pitting, pitting corrosion, salt water, salt water corrosion, sea water corrosion, seawater, stagnant salt water, stagnant water | Leave a comment
Posted on July 10, 2017 by dean
Q: I have a salt water environment with high velocities and a lot of debris including sand, dirt and particles. Because of the amount of debris, I’m concerned about what material would work best. A: Both Monel and Titanium can be good choices in this situation. Both perform extremely well … Continue reading →
Posted on April 7, 2017 by dean
Q: I have a seawater application where the water can be stagnant or polluted. Is Monel bolts the best choice? A: For stagnant seawater application we would usually suggest Titanium over Monel fasteners. Although Monel is very resistant to saltwater, it can experience pitting corrosion in stagnant water situations. There have … Continue reading →
Posted in Corrosion Resistance, FAQs, Specialty Metal Fasteners | Tagged Corrosion, Monel, seawater, Titanium | Leave a comment